Typical Tensile Properties
As welded | |||
Elongation | Tensile Strength | Yield Strength | 保护气体 |
17 % | 900 MPa | 800 MPa | ISO |
- | - | - | AWS |
夏比V型缺口冲击性能
As welded | ||
Impact Value | Testing Temperature | 保护气体 |
80 J | 20 °C | ISO |
焊缝金属分析
Mn | ||||
Mn | Mo | C | Si | Cr |
0.76 % | - | - | - | - |
Mo | ||||
Mn | Mo | C | Si | Cr |
- | 0.2 % | - | - | - |
C | ||||
Mn | Mo | C | Si | Cr |
- | - | 0.17 % | - | - |
Si | ||||
Mn | Mo | C | Si | Cr |
- | - | - | 0.52 % | - |
Cr | ||||
Mn | Mo | C | Si | Cr |
- | - | - | - | 1.15 % |
熔敷数据
Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
58 sec | 0.64 kg | 70.0 | 75-100 A | 0.90 kg/h | 20 V | 2.5 x 350 mm |
78 sec | 0.64 kg | 32.5 | 105-140 A | 1.40 kg/h | 21 V | 3.2 x 450 mm |
83 sec | 0.66 kg | 22.5 | 145-195 A | 1.90 kg/h | 22 V | 4.0 x 450 mm |
86 sec | 0.68 kg | 15.0 | 190-260 A | 2.80 kg/h | 23 V | 5.0 x 450 mm |