S450J0-Z25钢板化学成分和力学性能【舞阳钢铁办事处】
4. S450J0 Chemical composition % of the Product analysis of grade
|
C |
Si |
Mn |
Ni |
P |
S |
Cr |
Mo |
|
max 0.24 |
0.60 |
1.80 |
|
Max 0.040 |
Max 0.040 |
|
|
|
V |
Nb |
Ti |
N |
Cu |
|
|
|
|
|
|
|
0.027 |
0.60 |
|
|
|
5. S450J0 Mechanical Property
|
|
-150 |
150-250 |
250-400 |
||||||||||
|
Minimum energy nominal thickness Temperature(0) |
27 |
|
|
||||||||||
|
Nominal thickness (mm) |
to 16 |
16 - 40 |
40 - 63 |
63 - 80 |
80 - 100 |
100 - 150 |
150 - 200 |
200-250 |
250-400 |
||||
|
ReH - Minimum yield strength (MPa) |
450 |
430 |
410 |
390 |
380 |
380 |
|
|
|
||||
|
Nominal thickness (mm) |
-3 |
3-100 |
100-150 |
150-250 |
250-400 |
||||||||
|
Rm -Tensile strength (MPa) |
|
550-720 |
530-700 |
|
|
||||||||
|
Nominal thickness (mm) |
3-40 |
40-63 |
63-100 |
100-150 |
150-250 |
250-400 |
|||||||
|
A - Minimum elongation Lo = 5,65 √ So (%) |
17 |
17 |
17 |
17 |
|
|
|||||||
6. Equivalent grades of grade S450J0 (1.0590)
|
Germany DIN,WNr |
France AFNOR |
England BS |
Spain UNE |
Italy UNI |
Norway |
|
|
|
55C |
|
|
|
采用焊接连接的钢结构中，当钢板厚度不小于40 mm且承受沿板厚度方向的拉力时，为避免焊接时产生层状撕裂，需采用抗层状撕裂的钢材（通常简称为“Z向钢”）。厚板存在层状撕裂问题，故要提出Z向性能测试。
钢板和型钢经过滚轧成型的，一般多高层钢结构所用钢材为热轧成型，热轧可以破坏钢锭的铸造组织，细化钢材的晶粒。钢锭浇筑时形成的气泡和裂纹，可在高温和压力作用下焊合，从而使钢材的力学性能得到改善。然而这种改善主要体现在沿轧制方向上，因钢材内部的非金属夹杂物(主要为硫化物、氧化物、硅酸盐等)经过轧压后被压成薄片，仍残留在钢板中(一般yu钢板表面平行)，而使钢板出现分层（夹层）现象。这种非金属夹层现象。使钢材沿厚度方向受拉的性能恶化。因此钢板在三个方向的机械性能是有差别的：沿轧制方向1好；垂直于轧制方向的性能稍差；沿厚度方向性能又次之。
一般厚钢板较易产生层状撕裂，因为钢板越厚，非金属夹杂缺陷越多，且焊缝也越厚，焊接应力和变形也越大。为解决这个问题，1好采用Z向钢。这种钢板是在某一级结构钢（称为母级钢）的基础上，经过特殊冶练、处理的钢材，其含硫量为一般钢材的1/5以下，截面收缩率在15%以上。钢板沿厚度方向的受力性能(主要为延性性能)称为Z向性能。钢板的Z向性能可通过做试样拉伸试验得到，一般用断面收缩率来度量。我国生产的Z向钢板的标志是在母级钢钢号后面加上Z向钢板等级标志Z15、Z25、Z35，Z字后面的数字为截面收缩率的指标(%)。