Typical Tensile Properties
As welded | |||
Elongation | Tensile Strength | Yield Strength | 保护气体 |
28 % | 510 MPa | 400 MPa | ISO |
夏比V型缺口冲击性能
As welded | ||
Impact Value | Testing Temperature | 保护气体 |
70 J | 0 °C | ISO |
焊缝金属分析
Mn | ||
Mn | C | Si |
0.39 % | - | - |
C | ||
Mn | C | Si |
- | 0.07 % | - |
Si | ||
Mn | C | Si |
- | - | 0.44 % |
熔敷数据
Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
67 sec | 0.63 kg | 86 | 50-100 A | 0.63 kg/h | 23 V | 2.5 x 350 mm |
52 sec | 0.57 kg | 56 | 75-150 A | 1.25 kg/h | 25 V | 3.2 x 350 mm |
70 sec | 0.60 kg | 31 | 95-200 A | 1.65 kg/h | 25 V | 4.0 x 400 mm |
85 sec | 0.59 kg | 20 | 160-270 A | 2.1 kg/h | 25 V | 5.0 x 400 mm |